Thulium, 69Tm |
Ki-pún sèng-chit |
---|
Miâ, hû-hō | thulium, Tm |
---|
Gōa-hêng | silvery gray |
---|
Thulium tī chiu-kî-piáu lāi ê ūi-tì |
---|
|
Goân-chú-hoan | 69 |
---|
Goân-chú-liōng (±) | 168.93422(2)[1] |
---|
Goân-sò͘ lūi-pia̍t | lanthanum-hē |
---|
Cho̍k, hun-khu | n/a, f khu |
---|
Chiu-kî | tē 6 chiu-kî |
---|
Tiān-chú pâi-lia̍t | [Xe] 4f13 6s2 |
---|
per shell | 2, 8, 18, 31, 8, 2 |
---|
Bu̍t-lí sèng-chit |
---|
Siòng | solid |
---|
Iûⁿ-tiám | 1818 K (1545 °C, 2813 °F) |
---|
Hut-tiám | 2223 K (1950 °C, 3542 °F) |
---|
Bi̍t-tō͘ (sek-un) | 9.32 g·cm−3 |
---|
8.56 g·cm−3 |
Iûⁿ-hoà-jia̍t | 16.84 kJ·mol−1 |
---|
Cheng-hoat-jia̍t | 191 kJ·mol−1 |
---|
Jia̍t-iông-liōng | 27.03 J·mol−1·K−1 |
---|
cheng-khì-ap
P (Pa)
|
1
|
10
|
100
|
1 k
|
10 k
|
100 k
|
tī T (K)
|
1117
|
1235
|
1381
|
1570
|
(1821)
|
(2217)
| |
Goân-chú sèng-chit |
---|
Sng-hòa-sò͘ | 2, 3 (a basic oxide) |
---|
Tiān-hū-tō͘ | Pauling scale: 1.25 |
---|
Tiān-lī-lêng | 1st: 596.7 kJ·mol−1 2nd: 1160 kJ·mol−1 3rd: 2285 kJ·mol−1 |
---|
Goân-chú pòaⁿ-kèng | empirical: 176 pm |
---|
Kiōng-kè pòaⁿ-kèng | 190±10 pm |
---|
Cha̍p-lio̍k |
---|
Chiⁿ-thé kò͘-chō | hexagonal close-packed (hcp) |
---|
Jia̍t-phòng-tiòng | poly: 13.3 µm·m−1·K−1 (at r.t.) |
---|
Jia̍t-thoân-tō-lu̍t | 16.9 W·m−1·K−1 |
---|
Tiān-chó͘-lu̍t | poly: 676 nΩ·m (at r.t.) |
---|
Chû-sèng | paramagnetic (at 300 K) |
---|
Young hē-sò͘ | 74.0 GPa |
---|
Shear hē-sò͘ | 30.5 GPa |
---|
Bulk hē-sò͘ | 44.5 GPa |
---|
Poisson pí | 0.213 |
---|
Vickers ngē-tō͘ | 470–650 MPa |
---|
Brinell ngē-tō͘ | 470–900 MPa |
---|
CAS teng-kì pian-hō | 7440-30-4 |
---|
Le̍k-sú |
---|
Hō-miâ | after Thule, a mythical region in Scandinavia |
---|
Hoat-hiān kap siōng chá ê tông-ūi-sò͘ | Per Teodor Cleve (1879) |
---|
Chòe ún-tēng ê tông-ūi-sò͘ |
---|
Chú bûn-chiong: thulium ê tông-ūi-sò͘ |
|
Decay modes in parentheses are predicted, but have not yet been observed |
Thulium sī 1 ê hoà-ha̍k goân-sò͘. I ê goân-chú-hoan sī 69, hoà-ha̍k hû-hō sī Tm.